TM52 TiC titanium carbide based cermets steel bonded ferro-tic carbide and alloy rods, which contains a hard phase TiC and a bonding phase high manganese steel, wherein the bonding phase contains, by weight, Ni, Mn, and the balance elements. Hardness HRC 60-62, denstiy 6.2 ±0.2 g/cm3. TM52 steel bonded titanium carbide rod is widely used in mining industry, especially on high manganese steel crusher hammer with 3-5 times longer service life.
TM52 TiCtitanium carbide based cermets steel bonded ferro-ticcarbide and alloyrods, which contains a hard phase TiC and a bonding phase high manganese steel, wherein the bonding phase contains, by weight, Ni, Mn, and the balance elements. Hardness HRC 60-62, denstiy 6.2 ±0.2 g/cm3. TM52 steel bonded titanium carbide rod is widely used in mining industry, especially on high manganese steel crusher hammer with 3-5 times longer service life.
Advantage: Why Langfeng Material's steel bonded titanium carbide rod is better:
1:Use high purity raw material : Fe,Mn,Ni,and home made Titanium carbide powder,Strictly control in raw material ensure the high quality of TiC cermets rod;
2: Unique additive application ensure alloy grain densification;
3: Unique sintering process ensure stable quality.
Taking low-cost high-manganese steel or ultra-high manganese steel as large wear-resistant base material, casted with TM52 TiCtitanium carbide based cermets steel bonded ferro-ticcarbide and alloyrods, the new wear parts’s wearing side has excellent wear resistance, while non-wearing side with excellent plasticity and impact toughness.It has been successfully used for high manganese wear parts, like large jaw plate, rolling mortar wall, broken wall, vertical grinding roller, vertical grinding disc liner, counter-breaking plate hammer, installed by the user to use, consistent response is good.
Advantages:high wear resistance titanium carbide cermet rods evenly distributed in the work site, it effectively reduce the wearness of base high manganese steel material. So the service life of below wear parts in mining industry: crusher jaw, mill liner, hammer head, Vertical grinding roller, roller sets is enhaned at least 1.5 times, plus the maintenance and replacement are also significantly reduced;
TiC cermets rod’s hardness can not be higher than HRC62, HRC60 is the best. Once combined with high manganese steel substrate, surface hardning will happen under strong impact, that is the reason why the high manganese wear parts with titanium carbide steel boneded rod could get high wear resistance, while toughness and plasticity unchanged. If the hardness of TM52 TiCtitanium carbide based cermets steel bonded ferro-ticcarbide and alloyrods is too high, the rods will break during working.
TM52 titanium carbide cermet steel bonded carbide rod production method of high manganese steel hammer and process:
Die openings (Suitable for wooden mold, sand mold and EPC) → welding iron nails ( Welding the nail on the rod by argon arc which can fix the rod) → rods placed in a mold ( suitable wood mold, sand mold and EPC) → model coating (coating & drying each 3 times) → casting and sealing to finalized the design→ surface treatment.
TM52 TiCtitanium carbide based cermets steel bonded ferro-ticcarbide and alloyrods VS cemented carbide rods:
First of all, TM52 carbide-based titanium carbide cermet carbide rods cost is far lower than cemented carbide rods; Secondly TM52 TiCtitanium carbide based cermets steel bonded ferro-ticcarbide and alloyrods and high manganese steel substrate combined together, could play its greatest role . While cemented carbide rod could worked with both high manganese steel wear parts and high-chromium wear-resistant wear parts. Thirdly different processing methods, titanium carbide steel bonded rods are casting process, cemented carbide is generally mosaic process.
Below is the design chart we made for our European customer on the high manganese wear parts bottom side:
Properties |
Compostion(%) |
||
TRS (ISO 3327 ) |
1800 +200 N/mm2 |
Ni |
2 |
Hardness (ISO 3878 ) |
82.5±0.5 HRA |
TiC |
47 |
Density (ISO 3369 ) |
6.2 ±0.2 g/cm3 |
Fe |
37 |
Average Grain Size |
2.0 ±0.5μm |
Mn |
10 |
Porosities |
A02B00C00 |
Other |
4 |
TM52 TiCtitanium carbide based cermets steel bonded ferro-ticcarbide and alloyrods, our hot sale size is D12 x 50mm,D12 x 60mm,D14 x 40mm,D14 x 50mm,D14 x 60mm,D16 x 90mm, the size could be customized.